< Back to Articles
Physical Properties for Polyurethane 95A and 75A
Polyurethane 95A and 75A,
(Plei-Tech 22) 75A Sheet, Rod, & Tube/ 95A Sheet
|
Physical Properties |
Test Method |
Units |
Hardness |
|
Hardness A
Hardness D |
|
|
75 |
95 |
|
100% Modulus |
ASTM D412 |
psi |
480 |
1810 |
|
300% Modulus |
ASTM D412 |
psi |
1,000 |
3,600 |
|
Tensile Strength |
ASTM D412 |
psi |
4,600 |
7,000 |
|
Ultimate Elongation |
ASTM D412 |
% |
490 |
450 |
|
Split Tear |
ASTM D470 |
pli |
70 |
210 |
|
Die C Tear |
ASTM D624 |
pli |
350 |
690 |
|
Resilience |
ASTM D2632 |
% |
27 |
30 |
|
Compression Set (22 hours at 70°C) |
ASTM D385
Method B |
% |
30 |
35 |
|
Tear Abrasion (H-18 wheel 5000 cycles) |
D-1044-78 |
mg loss |
40 |
- |
|
Specific Gravity |
ASTM D792 |
|
1.22 |
1.26 |
Polyurethane 95A
(Plei-Tech 95) 95A Rod & Tube
|
Physical Properties |
Test Method |
Units |
Hardness |
|
Hardness A
Hardness D |
|
|
95
50 |
|
100% Modulus |
ASTM D412 |
psi |
2,200 |
|
300% Modulus |
ASTM D412 |
psi |
4,100 |
|
Tensile Strength |
ASTM D412 |
psi |
5,500 |
|
Ultimate Elongation |
ASTM D412 |
% |
350 |
|
Split Tear |
ASTM D470 |
pli |
125 |
|
Die C Tear |
ASTM D624 |
pli |
500 |
|
Resilience |
ASTM D2632 |
% |
42 |
|
Compression Set (22 hours at 70°C) |
ASTM D385 Method B |
% |
32 |
|
Compression Modulus
5%
10%
15%
20%
25% |
ASTM D575 |
psi |
500
840
1,200
1,650
2,100 |
|
Brittle Point |
ASTM D745 |
°F |
-94 |
|
Specific Gravity |
ASTM D792 |
|
1.13 |
The above valves are believed to be true to the best of Pleiger Plastics’ knowledge based upon information provided by raw material suppliers.
These values are to be used only as a guide, and are not to be construed as specifications.
Title: Physical Properties for Polyurethane 95A and 75A
Description: Physical and Mechanical Typical Properties.
Published: 1/22/2009
Last Edited: 9/18/2013
Information disclaimer:
The information contained in this article is for general information purposes only. The information is provided by
United States Plastic Corp. and while we endeavor to keep the information up to date and correct, we make no representations or
warranties of any kind, express or implied, about the completeness, accuracy, reliability, suitability or availability with
respect to the website or the information, products, services, or related graphics contained on the website for any purpose.
Any reliance you place on such information is therefore strictly at your own risk.
In no event will we be liable for any loss or damage including without limitation, indirect or consequential loss
or damage, or any loss or damage whatsoever arising from loss of materials, time or profits arising out of,
or in connection with, the use of this information.